Titanium Grade 5 | Ti-6Al-4V | Titanium Supplier Malaysia | Titanium Alloys | UNS R56400 | 3.7164 | ASTM B348
Price:
R.F.Q.
Share Product:
Detail
Grade 5 Titanium is the workhorse of all the titanium grades. Among all the titanium grades, the most commonly used titanium alloy is the Grade 5 titanium alloy (also known as Ti6Al4V, Ti-6Al-4V or Ti 6-4), it is formed with mixing pure titanium with 6% aluminium and 4% vanadium.
Its high strength, lightweight and corrosion resistance enable Titanium Grade 5 to be used in many applications. The most common market is aerospace, medical, marine and chemical processing industries. The alloy is also “age hardenable” by heat treatment to achieve even higher strengths.
--------
Ti 6AL-4V / Titanium Grade 5 is the best alloy for use in the creation of such things :
- Aircraft turbines
- Engine components
- Aircraft structural components
- Aerospace fasteners
- High-performance automatic parts
- Marine applications
- Sports equipment
Ti-6Al-4V
| Category | Titanium Alloy |
| Class | Wrought |
| Type | Alpha-beta alloy |
| Designations | United States: ASTM B265 Grade5, ASTM B348 Grade5, ASTM B381 Grade5, MIL-T-9046, MIL-T-9047, AMS 4928, AMS 4911, AMS 4906, AMS 4965 |
| Property | Typical Value |
| Density g/cm3 (lb/ cu in) | 4.42 (0.159) |
| Melting Range °C±15°C (°F) | 1649 (3000) |
| Specific Heat J/kg.°C (BTU/lb/°F) | 560 (0.134) |
| Volume Electrical Resistivity ohm.cm (ohm.in) | 170 (67) |
| Thermal Conductivity W/m.K (BTU/ft.h.°F) | 7.2 (67) |
| Mean Co-Efficient of Thermal Expansion 0-100°C /°C (0-212°F /°F) | 8.6×10-6 (4.8) |
| Mean Co-Efficient of Thermal Expansion 0-300°C /°C (0-572°F /°F) | 9.2×10-6 (5.1) |
| Beta Transus °C±15°C (°F) | 999 (1830) |
Table 2. Typical physical properties for Ti6Al4V
Mechanical Properties
| Property | Minimum | Typical Value |
| Tensile Strength MPa (ksi) | 897 (130) | 1000 (145) |
| 0.2% Proof Stress MPa (ksi) | 828 (120) | 910 (132) |
| Elongation Over 2 Inches % | 10 | 18 |
| Reduction in Area % | 20 | |
| Elastic Modulus GPa (Msi) | 114 (17) | |
| Hardness Rockwell C | 36 | |
| Specified Bend Radius | 4.5 | |
| Specified Bend Radius >0.070 in x Thickness | 5.0 | |
| Welded Bend Radius x Thickness | 6 | |
| Charpy, V-Notch Impact J (ft.lbf) | 24 (18) |
Table 3. Typical mechanical properties for Ti6Al4V.